Effect of fluoride-releasing adhesive systems in control of dental enamel hardness subjected to acid challenge
DOI:
https://doi.org/10.21270/archi.v6i5.2075Resumen
Purpose: To evaluate the effect of pH cycling with erosive solutions on the Knoop hardness of enamel restored with different fluoride-releasing materials. Methods: Eighteen selected bovine teeth were used and divided into 3 groups (n = 6) according to the restorative material used (Single Bond 2, One Up Bond F and Clearfil SE Protect). Three slices of each restored tooth were subjected to erosive pH cycling in acidic solutions (deionized water, citric acid and hydrochloric acid), with alternate phases of demineralization and remineralization. The microhardness recorded before and after erosive pH cycling was used to determine changes in the enamel. Results: Acidic solutions were able to change the hardness of enamel. After immersion in citric acid, the enamel restored with Clearfil SE Protect showed lesser mineral loss than the enamel restored with other materials at a distance of 30μm. There was an increase in the mineral loss after cycling with hydrochloric acid, compared to deionized water. In the distance of 70µm from adhesive interface, the enamel restored with Single Bond 2 showed greater mineral loss after immersion in citric acid. Conclusions: The fluoride present in Clearfil SE Protect adhesive system was able to protect the dental enamel against erosion process.Descriptors: Tooth Demineralization; Dental Enamel; Sodium Fluoride.
Descargas
Citas
Kim IH, Son JS, Min BK, Min BK, Kim YK, Kim KH, et al. A simple, sensitive and non-destructive technique for characterizing bovine dental enamel erosion: attenuated total reflection Fourier transforms infrared spectroscopy. Int J Oral Scie. 2016; 8:54-60.
Struzycka I, Rusyan E, Boquslawska-Kapala A. Tooth erosion- a multisciplinary approach. Pol Merkur Lekarski. 2016;40:79-83.
Kanzow P, Wegehaupt FJ, Attin T, Wiegand A. Etiology and pathogenesis of dental erosion. Quintessence Int. 2016;47 275-8.
Guedes APA, Moda MD, Suzuki TYU, Godas AGL, Sundfeld RH, Briso ALF, et al. Effect of fluoride-releasing adhesive systems on the mechanical properties of eroded dentin. Braz Dent J.2016; 27:153-9.
Kumar Y, Lohar J, Bhat S, Bhati M, Gandhi A, Mehta A. Comparative evaluation of demineralization of radicular dentin with 17% ethylenediaminetetraacetic acid, 10% citric acid, and MTAD at different time intervals: An in vitro study. J Int Soc Prev Community Dent.2016; 6 :44-8.
Conceição JM, Delbem AC, Danelon M, da Camara DM, Wiegand A, Pessan JP. Fluoride gel supplemented with sodium hemametaphosphate reduces enamel erosive wear in situ. J Dent. 2015; 43:1255-60.
Lippert F, Parker DM, Jandt KD. Susceptibility of deciduous and permanent enamel to dietary acid-induced erosion studied with atomic force microscopy nanoindentation. Eur J Oral Sci. 2004; 112:61-6.
Lippert F, Parker DM, Jandt KD. In vitro demineralization/remineralization cycles at human tooth enamel surfaces investigated by AFM and nanoindentation. J Colloid Interf Sci. 2004; 2:442-8.
Austin RS, Giusca CL, Macaulay G, Moazzez R, Bartlett DW. Confocal laser scanning microscopy and area-scale analysis used to quantify enamel surface textural changes from citric acid demineralization and salivary remineralization in vitro. Dent Mater. 2016;32:278-84.
Kirsten GA, Takahashi MK, Rached RN, Giannini M, Souza EM. Microhardness of dentin underneath fluoride-releasing adhesive systems subjected to cariogenic challenge and fluoride therapy. J Dent. 2010; 38:460-8.
Borges AB, Scaramucci T, Lippert F, Zero DT, Hara AT. Erosion protection by calclium lactate/sodium fluoride rinses under different salivary flows in vitro. Caries Res. 2014;48:193-9.
Barbour ME, Finke M, Parker DM, Hughes JA, Alenn GC, Addy M. The relationship between enamel softening and erosion caused by soft drinks at a range of temperatures. J Dent. 2006; 34:207-13.
Bartlett DW, Coward PY. Comparison of the erosive potential of gastric juice and carbonated drink in vitro. J Oral Rehabil. 2001; 28:1045-7.
Badra VV, Faraoni JJ, Ramos RP, Palma-Dibb RG: Influence of different beverages on the microhardness and surface roughness of resin composites. Oper Dent. 2005; 30:213-9.
Francisconi LF, Honório HM, Rios DAC, Magalhães AC, Machado MA, Buzalaf MA. Effect of erosive pH cycling on different restorative materials and on enamel restored with these materials. Oper Dent. 2008; 33:203-8.
Featherstone JD, Lussi A. Understanding the chemistry of dental erosion. Monogr Oral Sci. 2006;20: 66-76.
Imazato S, Ebi N, Takahashi Y, Kaneko T, Ebisu S, Russell RRB. Antibacterial activity of bactericide-immobilized filler for resin-based restoratives. Biomaterials. 2003; 24: 3605-9.
Itthagarun A, King NM, Wefel JS, Tay FR, Pashley DH. The effect of fluoridated and non-fluorited rewetting on in vitro recurrent caries. J Dent. 2001; 29: 255-73.
Pinto CF, Paes-Leme AF, Ambrosano GM, Giannini M. In vitro secondary caries inhibition by adhesive systems in enamel around composite restorations. Oper Dent. 2010; 35:345-52.
Imazato S, Kuramoto A, Takahashi Y, Ebisu S, Peters MC. In vitro antibacterial effects of the dentin primer of Clearfil Protect Bond. Dent Mater. 2006; 22: 527-32.
Wiegand A, Buchalla W, Attin T. Review on fluoride-releasing restorative materials – fluoride release and uptake characteristics, antibacterial activity and influence on caries formation. Dent Mater. 2007; 23: 343-62.
Hara AT, Queiroz CS, Giannini M, Serra MC, Cury JA. Fluoride release and secondary caries inhibition by adhesive systems on root dentin. Eur J Oral Sci. 2005; 113: 245-50.
Koshiro K, Sidhu SK, Inoue S, Ikeda T, Sano H. New concept of resin-dentin interfacial adhesion: the nano interaction zone. J Biomed Mater Res B Appl Biomater. 2006; 77:401-8.
Tay FR, Lai CNS, Chersoni S, Pashley DH, Mak YF, Suppa P, et al. Osmotic blistering in enamel bonded with one-step self-etch adhesives. J Dent Res. 2004; 83:290-5.
Perdigão J, Geraldeli S. Bonding characteristics of self-etching adhesives to intact versus prepared enamel. J Esthet Restor Dent. 2003; 15:32-41.
Hannig M, Bock H, Bott B, Hoth-Hannig W. Inter-crystallite nano retention of self-etching adhesives at enamel imaged by transmission electron microscopy. Eur J Oral Sci. 2002; 110: 464-70.